The challenge with ASA and ABS re:warping is chamber temps, not so much bed temperature. Both shrink pretty significantly compared to PLA and if your chamber is too cool and/or your print is too big or has difficult geometry you're going to be in for a rough time.
I'm curious about ASA & PTU currently, and looking into best practices (began my printing journey in 2018 w/ a Mk1S & a Phrozen Mini duo) before jumping in, so this is helpful info, thank you (& OP, et al). 🤓
3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at: or [email protected]
There are CAD communities available at: [email protected] or [email protected]
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
Be respectful, especially when disagreeing. Everyone should feel welcome here.
No porn (NSFW prints are acceptable but must be marked NSFW)
No Ads / Spamming / Guerrilla Marketing
Do not create links to reddit
If you see an issue please flag it
No guns
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe/ may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is 
Moderation policy: Light, mostly invisible